Princeton Engineers Develop New Cement That Is 17x More Crack-Resistant

Cement Composite Inspired by Shell Nacre

Engineers at Princeton have developed a cement composite inspired by nacre, or mother of pearl, making it 17 times more crack-resistant and 19 times more stretchable than standard cement. This bio-inspired composite, created by alternating layers of cement paste and polymer, could enhance the durability of various brittle ceramic materials. Experiments showed that beams with separated hexagonal tablets exhibited significant improvements in ductility and fracture toughness. While the findings are promising, further research is needed to apply these techniques in the field and to other ceramic materials. Credit: Sameer Khan/Fotobuddy

Princeton engineers developed a new cement composite inspired by shell nacre, significantly enhancing its durability and flexibility.

Engineers at Princeton University, drawing inspiration from the materials found in oyster and abalone shells, have developed a new cement composite. This innovative material is 17 times more resistant to cracking and 19 times more flexible and deformable without breaking compared to traditional cement. This breakthrough could significantly enhance the crack resistance of various brittle ceramic materials, ranging from concrete to porcelain.

“If we can engineer concrete to resist crack propagation, we can make it tougher, safer, and more durable,” said researcher Shashank Gupta, a graduate student in Reza Moini’s lab in the Department of Civil and Environmental Engineering.

In an article published June 10 in the journal Advanced Functional Materials, the research team led by Moini, an assistant professor of civil and environmental engineering, reported that creating alternating layers of tabulated cement paste and thin polymer can significantly increase crack resistance and the ability to deform without completely breaking (ductility).

Bio-Inspired Design and Testing

Moini’s lab often looks to biology for inspiration in its work on building materials. In this case, the team developed a composite inspired by a natural material called nacre, or mother of pearl, which is found inside certain shells. Gupta said that at the microscopic level, nacre consists of hexagonal tablets of the hard mineral aragonite glued together by a soft biopolymer.

The aragonite tablets contribute significantly to nacre’s strength, while the biopolymer adds flexibility and crack resistance. The toughening mechanism involves the aragonite tablets sliding under stress, which, along with other mechanisms, allows the nacre to dissipate energy. This sliding action, combined with the crack deflection and biopolymer deformation, enables nacre to endure substantial mechanical stress while maintaining its structural integrity, making it both strong and resilient.

Beams With Alternating Layers of Hexagonal Cement Tiles and Thin Polymer

The researchers created beams with alternating layers of hexagonal cement tiles and thin polymer. Credit: Sameer Khan/Fotobuddy

“This synergy between the hard and soft components is crucial to nacre’s remarkable mechanical properties,” Gupta said.

The Princeton team has developed innovative composites inspired by nacre, utilizing conventional construction materials like Portland cement paste combined with a limited amount of polymer. They alternated layers of cement paste sheets with a highly stretchable polymer, polyvinyl siloxane. The researchers created multi-layered small beams by alternating cement paste sheets with thin layers of polymer. These beams were then subjected to a notched three-point bending test, where each beam was tested under flexure to evaluate crack resistance (or fracture toughness).

Experimental Results and Observations

In the experiment, the researchers produced three types of beams. The first type consisted of alternating layers of cement paste sheets and thin polymer. For the second type, they used a laser to engrave hexagonal grooves into the cement paste sheets. These grooved sheets were then stacked with thin polymer layers in between. The third type was similar to the third, but the researchers cut through the cement completely, creating separated hexagonal tablets connected by the polymer layer. These cement-paste tablets lay atop the polymer layer similarly to how aragonite lies on the biopolymer layer in nacre. These three types were compared against a reference solid (monolithic) cast cement paste counterpart.

The experiments revealed that the failure of the reference beams was brittle — meaning that the beams broke suddenly and completely upon reaching their failure point, with no ductility. The beams with alternating layers, both grooved and non-grooved, demonstrated increased ductility and resistance to cracking.

The most significant results were observed in the beams with completely separated hexagonal tablets, which are similar to nacre. These beams exhibited 19 times the ductility and 17 times the fracture toughness while retaining nearly the same strength as the solid cement paste beam.

“Our bio-inspired approach is not to simply mimic nature’s microstructure but to learn from the underlying principles and use that to inform the engineering of human-made materials. One of the key mechanisms that makes a nacreous shell tough is the sliding of the tablet at the nanometer level. Here, we focus on the mechanism of tablet sliding by engineering the built-in tabulated structure of cement paste in balance with the properties of the polymer and the interface between them.” Moini said. “In other words, we intentionally engineer defects in the brittle materials as a way to make them stronger by design.“

The researchers noted that the findings are based on lab conditions and that it would take additional work and research to develop the techniques for use in the field. They are working to determine whether the structures’ fracture toughness and ductility apply to other ceramic materials beyond cement paste, such as concrete.

“We are only scratching the surface; there will be numerous design possibilities to explore and engineer the constitutive hard and soft material properties, the interfaces, and the geometric aspects that play into the fundamental size effects in construction materials,” Moini said.

Reference: “Tough and Ductile Architected Nacre-Like Cementitious Composites” by Shashank Gupta, Hadi S. Esmaeeli and Reza Moini, 10 June 2024, Advanced Functional Materials.
DOI: 10.1002/adfm.202313516

The project was funded in part by the National Science Foundation CAREER Award #2238992 through the Engineering for Civil Infrastructure program.

2 Comments on "Princeton Engineers Develop New Cement That Is 17x More Crack-Resistant"

  1. So, not even the modern building materials can go without some sort of carbon based chemicals. Now how’s that gonna work if they put down the oil industry?

  2. stephen p schaffer | June 26, 2024 at 8:20 am | Reply

    Why not simply copy the techniques and materials invented by the Romans? The Roman harbors built on the coast of Israel are over 2000 years old and are being measured and analyzed constantly.
    I haven’t seen any modern day concrete that comes with even a three hundred year warranty.

Leave a comment

Email address is optional. If provided, your email will not be published or shared.